| Property | Specification Requirement | Test Method | Test Value |
|---|---|---|---|
| Longitudinal Change | -10%~10% | ASTM D2671 | Pass |
| Concentration | ≥70% | ASTM D2671 | ≥70% |
| Tensile Strength | ≥10.3MPa | ASTM D2671 | ≥10.3MPa |
| Volume Resistivity | ≥10^15 Ω·cm | ASTM D2671 | ≥10^15 Ω·cm |
| Dielectric Strength | ≥39.37kV/mm | ASTM D2671 | ≥40kV/mm |
| Elongation at Break | ≥120% | ASTM D2671 | ≥140% |
| Heat Shock | No cracking | ASTM D2671 (180°C/4 hours) |
No cracking |
| Low-Temperature Flexibility | No cracking | ASTM D2671 (-55°C/4 hours) |
No cracking |
| No heavy metals | |||
| Gamma (y) and Ethylene Oxide (ETO) Sterilization | |||
| Product Code | Before Shrinking(mm) | After Shrinking (mm) | Standard Length (m) | ||
|---|---|---|---|---|---|
| Inside Diameter(Min.) | Wall Thickness | Inside Diameter (Max.) | Wall Thickness | ||
| Shrink Ratio 2.5:1 (Thick-Wall Type) | |||||
| MT2-0010 | 1.0 | 0.12±0.03 | 0.45 | 0.25±0.05 | 200 |
| MT2-0020 | 2.0 | 0.12±0.03 | 0.80 | 0.25±0.05 | 200 |
| MT2-0030 | 3.0 | 0.12±0.03 | 1.20 | 0.25±0.05 | 200 |
| MT2-0045 | 4.4 | 0.12±0.05 | 1.90 | 0.25±0.05 | 100 |
| MT2-0060 | 6.0 | 0.12±0.05 | 2.40 | 0.25±0.05 | 100 |
| MT2-0100 | 10.0 | 0.12±0.08 | 4.00 | 0.35±0.05 | 100 |