ㆍShrink ratio: 3:1
ㆍ Flexible, flame retardant
ㆍAbrasion and chemical resistance
ㆍReliable physical, chemical and electrical performance
ㆍ Flat tubes offer ease of printing
| Property | Specification Requirement | Test Method | Test Value |
|---|---|---|---|
| Longitudinal Change | ≤10% | ASTM D2671 | ≤5% |
| Tensile Strength | ≥10.3MPa | ASTM D2671 | ≥12MPa |
| Elongation at Break | ≥200% | ASTM D2671 | ≥400% |
| Elongation at Break After Aging | ≥100% | ASTM D2671 (175˚C/168 hours) |
≥400% |
| Heat Shock | No cracking | ASTM D2671 | No cracking |
| Low-Temperature Flexibility | No cracking | ASTM D2671 (-55˚C/4 hours) |
No cracking |
| Voltage Withstand | AC2500V/60S No damage |
ASTM D2671 | No damage |
| Dielectric Strength | ≥19.7kV/mm | ASTM D2671 | ≥25kV/mm |
| Volume Resistivity | ≥10^14Ω‧cm | ASTM D2671 | ≥10^14Ω‧cm |
| Copper Stability | No corrosion | ASTM D2671 | No corrosion |
| Print Performance | 20 back-and-forth rubbing cycles 20 back-and-forth rubbing cycles |
SAE AS5942 MIL-STD-202 |
Pass |
| Flammability | VW-1 | UL224 | Pass |
| Product Code | Product Size | Before Shrinking(mm) | After Shrinking (mm) | Packaging (pcs/box) | |
|---|---|---|---|---|---|
| mm | Inch | Inside Diameter(Min.) | Inside Diameter (Max.) | ||
| CTMS1353X0024 | 2.4 | 3/32 | 2.4 | 0.8 | 100 |
| CTMS1353X0032 | 3.2 | 1/8 | 3.2 | 1.1 | 100 |
| CTMS1353X0048 | 4.8 | 3/16 | 4.8 | 1.6 | 100 |
| CTMS1353X0064 | 6.4 | 1/4 | 6.4 | 2.1 | 100 |
| CTMS1353X0095 | 9.5 | 3/8 | 9.5 | 3.2 | 100 |
| CTMS1353X0127 | 12.7 | 1/2 | 12.7 | 4.2 | 100 |
| CTMS1353X0191 | 19.1 | 3/4 | 19.1 | 6.3 | 100 |
| CTMS1353X0254 | 25.4 | 1 | 25.4 | 8.5 | 100 |