| Property | Specification Requirement | Test Method | Test Value |
|---|---|---|---|
| Longitudinal Change | -15%~15% | ASTM D2671 | Pass |
| Tensile Strength | ≥10.3MPa | ASTM D2671 | ≥12MPa |
| Elongation at Break | ≥200% | ASTM D2671 | ≥400% |
| Tensile Strength After Aging | 70% of initial value | ASTM D2671 (158°C/168 hours) |
≥90% |
| Elongation at Break After Aging | ≥100% | ASTM D2671 (158°C/168 hours) |
≥300% |
| ภาวะช็อกจากความร้อน | No cracking | ASTM D2671 (200°C/4 hours) |
No cracking |
| Low-Temperature Flexibility | No cracking | ASTM D2671 (-30°C/1 hours) |
No cracking |
| Voltage Withstand | AC2500V/60SNo damage | ASTM D2671 | No damage |
| Volume Resistivity | ≥10^14 Ω·cm | ASTM D2671 | ≥10^14 Ω·cm |
| Copper Stability | No corrosion | ASTM D2671 (158°C/168 hours) |
No corrosion |
| Product Code | Size | Before Shrinking(mm) | After Shrinking (mm) | Standard Length (m) | ||||
|---|---|---|---|---|---|---|---|---|
| mm | Inch | Inside Diameter(Min.) | Wall Thickness (Nominal) | Inside Diameter (Max.) | Wall Thickness (Tube + Hot-Melt Adhesive) | Adhesive Thickness | ||
| AIS-C Shrink Ratio 3:1 | ||||||||
| AIS-C0032 | 3.2 | 1/8 | 3.2 | 0.45 | 1.0 | 1.00±0.28 | 0.45±0.10 | 200 |
| AIS-C0048 | 4.8 | 3/16 | 4.8 | 0.45 | 1.6 | 1.00±0.28 | 0.50±0.15 | 100 |
| AIS-C0064 | 6.4 | 1/4 | 6.4 | 0.50 | 2.0 | 1.00±0.28 | 0.50±0.15 | 100 |
| AIS-C0095 | 9.5 | 3/8 | 9.5 | 0.50 | 3.0 | 1.40±0.28 | 0.60±0.15 | 50 |
| AIS-C0127 | 12.7 | 1/2 | 12.7 | 0.65 | 4.0 | 1.78±0.38 | 0.76±0.20 | 1.22 |
| AIS-C0150 | 15.0 | 5/8 | 15.0 | 0.60 | 5.0 | 1.90±0.38 | 0.76±0.20 | 1.22 |
| AIS-C0191 | 19.1 | 3/4 | 19.1 | 0.70 | 6.0 | 2.25±0.55 | 0.76±0.20 | 1.22 |
| AIS-C0254 | 25.4 | 1 | 25.0 | 0.80 | 8.0 | 2.54±0.55 | 1.00±0.25 | 1.22 |
| AIS-C0381 | 38.1 | 1 1/2 | 38.1 | 0.80 | 13.0 | 2.54±0.55 | 1.00±0.25 | 1.22 |