| Property | Specification Requirement | Test Method | Test Value |
|---|---|---|---|
| Longitudinal Change | -10%~10% | ASTM D2671 | Pass |
| Tensile Strength | ≥10.3MPa | ASTM D2671 | ≥11.3MPa |
| Elongation at Break | ≥200% | ASTM D2671 | ≥400% |
| Tensile Strength After Aging | 70% of initial value | ASTM D2671 (158°C/168 hours) | ≥80% |
| Elongation at Break After Aging | ≥100% | ASTM D2671 (158°C/168 hours) | ≥200% |
| ภาวะช็อกจากความร้อน | No cracking | ASTM D2671 (200°C/4 hours) | No cracking |
| Low-Temperature Flexibility | No cracking | ASTM D2671 (-55°C/4 hours) | No cracking |
| Voltage Withstand | AC2500V/60SNo damage | ASTM D2671 | No damage |
| Volume Resistivity | ≥10^14 Ω·cm | ASTM D2671 | ≥10^14 Ω·cm |
| Insulation Performance | ≥19.7kV/mm | ASTM D2671 | 22 kV/mm |
| Flammability | VW-1 | UL224 | Pass |
| Product Code | Size | Before Shrinking(mm) | After Shrinking (mm) | Standard Length (m) | |||
|---|---|---|---|---|---|---|---|
| mm | Inch | Inside Diameter | Wall Thickness | Inside Diameter (Max.) | Wall Thickness (Min.) | ||
| G5-YG0015 | 1.5 | 1/16 | 2.0±0.3 | 0.20±0.05 | 0.8 | 0.36 | 200 |
| G5-YG0025 | 2.5 | 3/32 | 3.0±0.3 | 0.25±0.05 | 1.25 | 0.44 | 200 |
| G5-YG0030 | 3.0 | 1/8 | 3.5±0.3 | 0.25±0.05 | 1.50 | 0.44 | 200 |
| G5-YG0045 | 4.5 | 3/16 | 5.0±0.3 | 0.25±0.05 | 2.25 | 0.44 | 100 |
| G5-YG0060 | 6.0 | 1/4 | 6.5±0.3 | 0.28±0.05 | 3.0 | 0.56 | 100 |
| G5-YG0080 | 8.0 | 5/16 | 8.6±0.3 | 0.30±0.07 | 4.0 | 0.56 | 100 |
| G5-YG0090 | 9.0 | 3/8 | 9.6±0.3 | 0.30±0.07 | 4.5 | 0.56 | 100 |
| G5-YG0120 | 12.0 | 1/2 | 12.7±0.4 | 0.30±0.07 | 6.0 | 0.56 | 100 |
| G5-YG0160 | 16.0 | 5/8 | 16.7±0.5 | 0.35±0.08 | 8.0 | 0.69 | 100 |
| G5-YG0180 | 18.0 | 3/4 | 19.0±0.5 | 0.40±0.10 | 9.0 | 0.77 | 100 |
| G5-YG0250 | 25.0 | 1 | 26.0±1.0 | 0.45±0.10 | 12.5 | 0.87 | 50 |
| G5-YG0300 | 30.0 | 1 1/4 | 31.5±1.0 | 0.45±0.10 | 15.0 | 0.87 | 50 |
| G5-YG0400 | 40.0 | 1 1/2 | 41.5±1.0 | 0.50±0.10 | 20.0 | 0.87 | 50 |
| G5-YG0500 | 50.0 | 2 | 51.5±1.0 | 0.55±0.10 | 25.0 | 0.97 | 25 |